What material is the electrode made of? There are many types of welding rods. The more common ones on the market are silver welding rods, stainless steel welding rods, cast iron welding rods, carbon steel welding rods, aluminum welding rods, low alloy steel welding rods, cobalt-based welding rods, etc. Welding electrodes are divided into wear-resistant electrodes, universal electrodes and other categories. The electrode type has a lot to do with its usage and usefulness, so let's learn about the electrode type and use together!

1. What material is the electrode made of?

The electrode is to apply the coating (coating) evenly and centripetally on the welding core outside the metal welding core. The welding core is the metal core of the electrode. In order to ensure the quality and performance of the weld, there are strict regulations on the content of each metal element in the welding core, especially the content of harmful impurities (such as sulfur, phosphorus, etc.), which should be strictly controlled. The limit is better than that of the base metal. The electrode is composed of two parts: the welding core and the coating. Different types have different solder cores. Here are some common electrodes:

1. Silver electrode

Silver electrode is a kind of electrode with silver or silver-based solid body, which has excellent process performance, low melting point, good wettability and ability to fill gaps, and has high strength, good plasticity, and electrical conductivity. It has excellent corrosion resistance and can be used to braze all black and non-ferrous metals except aluminum, magnesium and other low melting point metals. This product is widely used in refrigeration, lighting, hardware and electrical appliances, instrumentation, chemical industry, aerospace and other industrial manufacturing field.

2. Stainless steel electrode

Stainless steel electrode refers to a type of electrode coated with stainless steel as raw material. It can be divided into chrome stainless steel electrode and chrome nickel stainless steel electrode, which are widely used in chemical, fertilizer, petroleum, medical machinery manufacturing and other industries. In addition to meeting the general welding process performance and the mechanical properties of the welded joint, the stainless steel electrode must also ensure that the welded joint can meet certain corrosion resistance requirements.

3. Cast iron electrode

Cast iron electrode is an electrode used for cast iron, which is characterized by high strength and good plasticity. Suitable for gray cast iron and ductile iron, and can be machined. Cast iron is an iron-carbon alloy with a carbon content greater than 2%. There are more than 10 kinds of cast iron electrodes available in China, which can be selected according to different cast iron materials, different machining requirements and the importance of welding repair parts.

Due to the high carbon content, uneven structure and low plasticity of cast iron, it is a material with poor weldability. In the welding process, defects such as white mouth, cracks and pores are easily generated. Therefore, cast iron welding repairs also require higher technical proficiency for welders. Cast iron welding repairs can be roughly divided into two types: preheating welding and cold welding.

4. Carbon steel electrode

Carbon steel electrodes (the tensile strength of the deposited metal is less than or equal to 500MPa or 50kgf/mm2) are suitable for carbon steel and low-strength low-alloy steel welding.

For low-hydrogen type and iron powder type electrodes, the electrode must be baked at 350°C or higher before welding, and it should be done as much as possible. cracks, deterioration of process performance, etc.). For cellulose-type electrodes, the baking temperature should be strictly followed. If the temperature is too high, the cellulose in the coating will be burned off and the inherent process performance of the electrode will be destroyed.

2. Types and uses of welding rods

1. SH.J422

It is used for welding more important low carbon steel structures and low alloy steels with low strength grades such as Q235.

Description: J422 is a carbon steel electrode with titanium calcium type coating. It has excellent welding process performance, stable arc, beautiful weld bead, small spatter, both AC and DC, and can be used for all-position welding.

Uses: Used for welding important low carbon steel structures and low alloy steels with low strength grades, such as Q235.

2. SH.J426

For welding important low carbon steel and low alloy structures. Has good mechanical properties and crack resistance. It needs to be baked at 350°C xlh before use.

Description: J426 is a carbon steel electrode with low hydrogen potassium type coating. Has good mechanical properties and crack resistance. AC and DC dual-use, can perform all-position welding.

Application: Used for welding important low carbon and low alloy steel structures.

3. SH.J427

For welding important low carbon steel and low alloy structures. It has good plasticity, toughness and crack resistance. It needs to be baked at 350°C xlh before use.

Description: J427 is a carbon steel electrode with low hydrogen sodium type coating. With DC reverse connection, all-position welding can be performed, and it has excellent plasticity, toughness and crack resistance.

Application: Used for welding important low carbon steel and low alloy steel structures.

4. SH.J506

For welding of mild and medium carbon steels. Has good mechanical properties and crack resistance. It needs to be baked at 350°C xlh before use.

Description: J506 is a carbon steel electrode with low hydrogen potassium type coating. Has good mechanical properties and crack resistance. AC and DC dual-use, can perform all-position welding.

Application: Used for welding medium carbon steel and low carbon steel.

5. SH.J507

Can weld medium carbon steel and some low alloy steels. It adopts DC arc welding current reverse connection, which has good plasticity, toughness and crack resistance. It needs to be baked at 350°C xlh before use.

Description: 507 is a carbon steel electrode with low hydrogen sodium type coating. With DC reverse connection, all-position welding can be performed. The weld metal has good plasticity, toughness and crack resistance.

Application: It can weld medium carbon steel and some low alloy steel.

5. A402 (E310-16)

Description: A402 is a pure austenitic stainless steel electrode with titanium calcium type coating. The deposited metal has excellent oxidation resistance under the high temperature condition of 900℃-1000℃. AC and DC dual-use, with good operating performance.

Uses: It is used for welding of the same type of heat-resistant stainless steel working under high temperature conditions, and can also be used for welding of chromium steels with high hardening (such as chromium, molybdenum, chromium, molybdenum, chromium 13, chromium 28, etc.) and dissimilar steels.

RELATED NEWS

MORE
What material is the electrode made of, the type and use of the electrode

What material is the electrode made of, the type and use of the electrode

What material is the electrode made of? There are many types of welding rods. The more common ones on the market are silver welding rods, stainless steel welding rods, cast iron welding rods, carbon steel welding rods, aluminum welding rods, low alloy steel welding rods, cobalt-based welding rods, etc. Welding electrodes are divided into wear-resistant electrodes, universal electrodes and other categories. The electrode type has a lot to do with its usage and usefulness, so let's learn about the electrode type and use together!1. What material is the electrode made of?The electrode is to apply the coating (coating) evenly and centripetally on the welding core outside the metal welding core. The welding core is the metal core of the electrode. In order to ensure the quality and performance of the weld, there are strict regulations on the content of each metal element in the welding core, especially the content of harmful impurities (such as sulfur, phosphorus, etc.), which should be strictly controlled. The limit is better than that of the base metal. The electrode is composed of two parts: the welding core and the coating. Different types have different solder cores. Here are some common electrodes:1. Silver electrodeSilver electrode is a kind of electrode with silver or silver-based solid body, which has excellent process performance, low melting point, good wettability and ability to fill gaps, and has high strength, good plasticity, and electrical conductivity. It has excellent corrosion resistance and can be used to braze all black and non-ferrous metals except aluminum, magnesium and other low melting point metals. This product is widely used in refrigeration, lighting, hardware and electrical appliances, instrumentation, chemical industry, aerospace and other industrial manufacturing field.2. Stainless steel electrodeStainless steel electrode refers to a type of electrode coated with stainless steel as raw material. It can be divided into chrome stainless steel electrode and chrome nickel stainless steel electrode, which are widely used in chemical, fertilizer, petroleum, medical machinery manufacturing and other industries. In addition to meeting the general welding process performance and the mechanical properties of the welded joint, the stainless steel electrode must also ensure that the welded joint can meet certain corrosion resistance requirements.3. Cast iron electrodeCast iron electrode is an electrode used for cast iron, which is characterized by high strength and good plasticity. Suitable for gray cast iron and ductile iron, and can be machined. Cast iron is an iron-carbon alloy with a carbon content greater than 2%. There are more than 10 kinds of cast iron electrodes available in China, which can be selected according to different cast iron materials, different machining requirements and the importance of welding repair parts.Due to the high carbon content, uneven structure and low plasticity of cast iron, it is a material with poor weldability. In the welding process, defects such as white mouth, cracks and pores are easily generated. Therefore, cast iron welding repairs also require higher technical proficiency for welders. Cast iron welding repairs can be roughly divided into two types: preheating welding and cold welding.4. Carbon steel electrodeCarbon steel electrodes (the tensile strength of the deposited metal is less than or equal to 500MPa or 50kgf/mm2) are suitable for carbon steel and low-strength low-alloy steel welding.For low-hydrogen type and iron powder type electrodes, the electrode must be baked at 350°C or higher before welding, and it should be done as much as possible. cracks, deterioration of process performance, etc.). For cellulose-type electrodes, the baking temperature should be strictly followed. If the temperature is too high, the cellulose in the coating will be burned off and the inherent process performance of the electrode will be destroyed.2. Types and uses of welding rods1. SH.J422It is used for welding more important low carbon steel structures and low alloy steels with low strength grades such as Q235.Description: J422 is a carbon steel electrode with titanium calcium type coating. It has excellent welding process performance, stable arc, beautiful weld bead, small spatter, both AC and DC, and can be used for all-position welding.Uses: Used for welding important low carbon steel structures and low alloy steels with low strength grades, such as Q235.2. SH.J426For welding important low carbon steel and low alloy structures. Has good mechanical properties and crack resistance. It needs to be baked at 350°C xlh before use.Description: J426 is a carbon steel electrode with low hydrogen potassium type coating. Has good mechanical properties and crack resistance. AC and DC dual-use, can perform all-position welding.Application: Used for welding important low carbon and low alloy steel structures.3. SH.J427For welding important low carbon steel and low alloy structures. It has good plasticity, toughness and crack resistance. It needs to be baked at 350°C xlh before use.Description: J427 is a carbon steel electrode with low hydrogen sodium type coating. With DC reverse connection, all-position welding can be performed, and it has excellent plasticity, toughness and crack resistance.Application: Used for welding important low carbon steel and low alloy steel structures.4. SH.J506For welding of mild and medium carbon steels. Has good mechanical properties and crack resistance. It needs to be baked at 350°C xlh before use.Description: J506 is a carbon steel electrode with low hydrogen potassium type coating. Has good mechanical properties and crack resistance. AC and DC dual-use, can perform all-position welding.Application: Used for welding medium carbon steel and low carbon steel.5. SH.J507Can weld medium carbon steel and some low alloy steels. It adopts DC arc welding current reverse connection, which has good plasticity, toughness and crack resistance. It needs to be baked at 350°C xlh before use.Description: 507 is a carbon steel electrode with low hydrogen sodium type coating. With DC reverse connection, all-position welding can be performed. The weld metal has good plasticity, toughness and crack resistance.Application: It can weld medium carbon steel and some low alloy steel.5. A402 (E310-16)Description: A402 is a pure austenitic stainless steel electrode with titanium calcium type coating. The deposited metal has excellent oxidation resistance under the high temperature condition of 900℃-1000℃. AC and DC dual-use, with good operating performance.Uses: It is used for welding of the same type of heat-resistant stainless steel working under high temperature conditions, and can also be used for welding of chromium steels with high hardening (such as chromium, molybdenum, chromium, molybdenum, chromium 13, chromium 28, etc.) and dissimilar steels.